410 Stainless Steel Plate

410 stainless steel is a commonly used martensitic stainless steel whose main components are iron, carbon, chromium and a small amount of other elements.
Wechat : +86 15165828999

Product Description

  • Commodity name: 410 Stainless Steel Plate

410 stainless steel is a commonly used martensitic stainless steel whose main components are iron, carbon, chromium and a small amount of other elements.

410 Stainless Steel Plate Description

410 stainless steel is a type of martensitic stainless steel with a chromium content of 11.5% and excellent corrosion resistance. 410 stainless steel has been quenched, tempered and polished to improve corrosion resistance. And quenching and tempering just makes 410 stainless steel harder. Compared to austenitic stainless steel, martensitic stainless steel is relatively inferior, which is why martensitic stainless steel requires a final heat treatment to be manufactured. Grade 410 stainless steel has the ability to withstand hot gases, steam, food, weak acids and bases, fresh water, and dry air. This steel is hardened for maximum corrosion and heat resistance. 410 stainless steel is a versatile and popular choice in automotive manufacturing due to its many advantages. A key advantage of this material is its high strength, making it ideal for applications requiring durability and wear resistance.


Product Parameters

Product Name

410 Stainless Steel Plate

Type

Plate

Thickness

0.3mm-200mm

Length

2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.

Width

40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.

Standard

ASTM, AISI, JIS, GB, DIN, EN, etc.

Surface

BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.

Scope of Application

Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging,

Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.

Certificate

ISO, SGS, BV, etc.

Production Technology

Hot Rolling, Cold Rolling

Edge Processing

Edging, Trimming

 

Chemical Composition

C

Si

Mn

Cr

Ni

S

P

≤ 0.15

≤1.0

≤1.0

11.5～13.5

≤ 0.5

≤ 0.03

≤ 0.04

 

Mechanical Properties

Tensile Strength Kb (MPa)

Yield Strength σ0.2 (MPa)

Elongation D5 (%)

Hardness

≥450

≥205

≥20

≤ 201HB

 

Physical Performance

Density(g/cm³)

Modulus of Elasticity(Gpa)

Coefficient of Thermal Expansion(10-6/°C)

Coefficient of Thermal Conductivity(W/m*K)

Resistivity(ΜΩ. cm)

7.74

200

9.9

24.9

570

 

Surface Selection


Product Show

Factory Show

Customer Visit

Message

Requiredwrong format
Requiredwrong format
Requiredwrong format
Required

Products Recommended

©  Hongye Steel (Shandong) Co., Ltd. Rights Reserved